Baked Core

แปลว่า(english) A core which has been heated through sufficient time and temperature to produce the desired physical properties attainable from its oxidizing or thermal-setting binders.

Burning 2

แปลว่า(english) Heating a metal beyond the temperature limits allowable for the desired heat treatment, or beyond the point where serious oxidation or other detrimental action begins.

Cure

แปลว่า(Concrete Engineering) Method of maintaining sufficient internal humidity and proper temperature for freshly placed concrete to assure proper hydration of the cement, and proper hardening of the concrete.

Water Vapor Pressure

แปลว่า(Concrete Engineering) The pressure exerted by water vapor. Air that contains higher amounts of water vapor exerts a higher vapor pressure than air which has a lower amount of has a higher water vapor pressure In concrete water vapor pressure is calculated by the difference between the vapor pressure of the concrete and the ambient relative humidity and temperature and in contact with the soil. that is calculated by; based upon relative humidity and temperature. The greater the difference between the water vapor and ambient humidity and temperature, in degrees Fahrenheit. the greater the water vapor pressure exerted.

Braze Welding

แปลว่า(english) A family of welding procedures where metals are joined by filler metal that has a melting temperature below the solidus of the parent metal, but above 840 (450 C).

Troposphere

แปลว่า(Environmental Engineering) The lower atmosphere, from the earth's surface to approximately 12 km. This portion of the earth's atmosphere contains about 95 percent of the atmospheric gases. The temperature gradually declines through this region.

Blue Brittleness 2

แปลว่า(english) Reduced ductility occurring as a result of strain aging, when certain ferrous alloys are worked between 300 and 700 (degrees) F. This phenomenon may be observed at the working temperature or subsequently at lower temperatures.

Cement, Portland (ASTM C150) (Concrete Engineering)

แปลว่าA powdery substance made by burning, at a high temperature, a mixture of clay and limestone producing lumps called “clinkers” which are ground into a fine powder consisting of hydraulic calcium silicates. For non-portland cements, see aluminous cement.

Blue Annealing

แปลว่า(english) Heating hot rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental.

Box Annealing 2

แปลว่า(english) A process of annealing a ferrous alloy in a closed metal container, with or without packing materials, in order to minimize the effects of oxidation. The charge is normally heated slowly to a temperature below the transformation range, but occasionally above or within it, and then is slowly cooled.

Box Annealing

แปลว่า(english) Annealing a metal or alloy in a sealed container under conditions that minimize oxidation. In box annealing a ferrous alloy, the charge is usually heated slowly to a temperature below the transformation range, but sometimes above or within it, and is then cooled slowly; this process is also called close annealing or pot annealing.

Moist Room

แปลว่า(Concrete Engineering) A room used for storing and curing cementitious test specimens. The atmosphere of this room is maintained at a temperature of 73.4 3.0'F or 23.0*1.7'0 and relative humidity of at least 98 percent. These facilities must be adequate to continually maintain free moisture on the exteriors of test specimens.