Change of State

แปลว่า(Concrete Engineering) The process whereby liquid is heated to the point of evaporation changing the liquid into a gas the condensation of a gas on a cooler surface returning it from gaseous to liquid form.

Rock Pocket

แปลว่า(Concrete Engineering) Area or portion of hardened concrete which is deficient in mortar and consisting primarily of coarse aggregate and open voids; caused by insufficient consolidation or separation during placement, or both; by leakage from form.

Slump Cone

แปลว่า(Concrete Engineering) A metal mold in the form of a truncated cone with a top diameter of 4”, a bottom diameter of 8”, and a height of 12”, used to fabricate the specimen for a slump test.

ASR - Alkali-Silica Reactivity

แปลว่า(Concrete Engineering) The reaction of aggregates, which contain some form of silica or carbonates with sodium oxides or potassium oxides in cement, particularly in warm, moist climates or environments, causing expansion, cracking or popouts in concrete.

ทองขาว

หมายถึง(โบ) น. โลหะสีขาวแกมเทา บุเป็นแผ่นรีดเป็นลวดได้ อาจหมายถึงโลหะนิกเกิล หรือโลหะแพลทินัม ก็ได้; ส่วนประกอบส่วนหนึ่งของจานจ่ายไฟในเครื่องยนต์ของรถยนต์ ทำหน้าที่เป็นทางเดินของกระแสไฟฟ้าแรงตํ่า และทำให้กระแสไฟฟ้าแรงตํ่าขาดวงจรเพื่อให้เกิดกระแสไฟฟ้าแรงสูงที่คอยล์ (coil) เป็นผลให้มีประกายไฟฟ้าขึ้นที่ปลายเขี้ยวของหัวเทียนในจังหวะที่ถูกต้อง.

HRM High Reactivity Metakaolin

แปลว่า(Concrete Engineering) Refined form of an ASTM C618, Class N (natural) pozzolan. A high performance, mineral admixture, similar in performance to silica fume, additionally comparable in cost. Pure white powdered in form will, not effect the natural color or darken concrete as silica fume does. Suitable for high-performance color matching in architectural concrete. Dosage at 5% to 10%, of cement by weight. No bleed water, better finishability, more creamy, cleanup is easier with slightly higher 28 day strengths and 25% - 35% less plasticizer is required than silica fume.

Black Plate

แปลว่า(english) A light weight or a thin uncoated steel sheet or strip so called because of its dark oxide coloring prior to pickling. It is manufactured by two different processes. (1) Form sheet bar on single stand sheet mills or sheet mills in tandem. This method is now almost obsolete. (2) On modern, high speed continuous tandem cold reduction mills from coiled hot rolled pickled wide strip into ribbon wound coils to finished gage. Sizes range from 12 to 32 in width, and in thicknesses from 55 lbs. to 275 lbs. base box weight. It is used either as is for stampings, or may be enameled or painted or tin or terne coated.

Brazing

แปลว่า(english) Joining metals by fusion of nonferrous alloys that have melting points above 800 F (425C), but lower than those of the metals being joined. May be accomplished by a torch. Filler metal is ordinarily in rod form in torch brazing; whereas in furnace and dip brazing the work material is first assembled and the filler metal may then be applied as wire, washers, clips, bands, or may be bonded, as in brazing sheet.

Z-Mill

แปลว่า(english) The full name for z-mill is Sendzimir mill. A Z-mill operates with a very small diameter work roll, normally about 2 inches, backed up by a number of rolls in a pyramid-shaped stack. This roll set up allows you to exert extremely high forces through the work roll and yet keep the work roll from extreme flexing. The take-up roll on the Z-Mill also exerts a tension on the coil as it comes through the mill. The combination of high pressure and tension makes the mill capable of rolling material thin and flat.