ผลการค้นหา

Blue Annealing

แปลว่า(english) Heating hot rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental.

Hydrogenesis

แปลว่า(Concrete Engineering) Another term for condensation. The term is especially applied to base and soil substrates under highway pavements. where the barometric pump causes the inhalation of humid air, which then condenses in those structures, causing an ever increasing moisture content and sometimes instability.

Back Rake

แปลว่า(english) The angular surface ground back from the cutting edge of cutting tools. On lathe cutting tools. The rake is positive if the face slopws down from the cutting edge toward the shank, and negative if the face sloopes upward toward the shank.

Brinell Hardness

แปลว่า(english) The hardness of a metal or part, as represented by the number obtained from the ratio between the load applied on the spherical area of the impression made by a steel ball forced into the surface of the material tested.

Basic Oxygen Process 2

แปลว่า(english) A steel making process wherein oxygen of the highest purity is blown onto the surface of a bath of molten iron contained in a basic lined and ladle shaped vessel. The melting cycle duration is extremely short with quality comparable to Open Hearth Steel.

Pozzolan (ASTM C 618)

แปลว่า(Concrete Engineering) A siliceous, or siliceous and aluminous material, which in itself possesses little or no cementitious value but will, in a finely divided form, such as a powder or liquid and in the presence of moisture, chemically react with calcium hydroxide at ordinary temperatures to form permanent, insoluble compounds possessing cementitious properties.

Carbonation

แปลว่า(Concrete Engineering) 1) Reaction between the products of portland cement (soluble calcium hydroxides), water and carbon dioxide to produce insoluble calcium carbonate (efflorescence). 2) Soft white, chalky surface dusting of freshly placed, unhardened concrete caused by carbon dioxide from unvented heaters or gasoline powered equipment in an enclosed space. 3) Carbonated, dense, impermeable to absorption, top layer of the surface of concrete caused by surface reaction to carbon dioxide. This carbonated layer becomes denser and deeper over a period of time. 4) Reaction with carbon dioxide which produces a slight shrinkage in concrete. Improves chemical stability. Concrete masonry units during manufacturing may be deliberately exposed to carbon dioxide after reaching 80% strength to induce carbonation shrinkage to make the units more dimensionally stable. Future drying shrinkage is reduced by as much as 30%.

Pressure:

แปลว่า(english) Pressure is a similar idea to stress, the force intensity at a point, except that pressure means something acting on the surface of an object rather than within the material of the object. When discussing the pressure within a fluid, the meaning is equivalent to stress.

Concentrated force:

แปลว่า(english) A force considered to act along a single line in space. Concentrated forces are useful mathematical idealizations, but cannot be found in the real world, where all forces are either body forces acting over a volume or surface forces acting over an area.

Moist Room

แปลว่า(Concrete Engineering) A room used for storing and curing cementitious test specimens. The atmosphere of this room is maintained at a temperature of 73.4 3.0'F or 23.0*1.7'0 and relative humidity of at least 98 percent. These facilities must be adequate to continually maintain free moisture on the exteriors of test specimens.

Boil

แปลว่า(english) Agitation of a bath of metal caused by the liberation of a gas beneath its surface. May be deliberately induced by the addition of oxidizing material to a bath containing excess carbon. In the later case it is called a carbon boil and CO or CO2 are liberated.

Nitrification

แปลว่า(Environmental Engineering) The biological oxidation of ammonia and ammonium sequentially to nitrite and then nitrate. It occurs naturally in surface waters, and can be engineered in wastewater treatment systems. The purpose of nitrification in wastewater treatment systems is a reduction in the oxygen demand resulting from the ammonia.